486 siemens matsushita components combination: elp 22/6/16 with elp 22/6/16 elp 22/6/16 magnetic characteristics (per set) s l/a = 0,41 mm C1 l e = 32,5 mm a e = 78,3 mm 2 a min = 77,9 mm 2 v e = 2540 mm 3 approx. weight 13 g/set ungapped calculation factors (see page 423 for formulas) elp 22/6/16 + elp 22/6/16: validity range: k1 , k2 : 0,10 mm < s < 1,50 mm k3 , k4 : 100 nh < a l < 700 nh material a l value nh m e a l1min nh p v w/set ordering code (per piece) n49 3100 25 % 1010 1840 < 0,65 (50 mt, 500 khz, 100 ?c) b66285-g-x149 n87 4500 25 % 1470 2760 < 1,50 (200 mt, 100 khz, 100 ?c) b66285-g-x187 material relationship between air gap C a l value calculation of saturation current k1 (25 ?c) k2 (25 ?c) k3 (25 ?c) k4 (25 ?c) k3 (100 ?c) k4 (100 ?c) n87 126 C 0,814 232 C 0,796 200 C 0,873 fek0339-r 5 0,1 3 3,20,1 r0,8 5,70,1 16,8 0,4 15,8 0,3 21,8 0,4 elp 22/6/16 core b66285
siemens matsushita components 487 combination: elp 22/6/16 with i 22/2,5/16 elp 22/6/16 i 22/2,5/16 magnetic characteristics (per set) s l/a = 0,33 mm C1 l e = 26,1 mm a e = 78,5 mm 2 a min = 77,9 mm 2 v e = 2050 mm 3 approx. weight 10,5 g/set ungapped calculation factors (see page 423 for formulas) elp 22/6/16 + i 22/2,5/16: validity range: k1 , k2 : 0,10 mm < s < 1,50 mm k3 , k4 : 100 nh < a l < 700 nh clamp ordering code per piece, 2 pieces required ordering code: b65804-p2204 material a l value nh m e a l1min nh p v w/set ordering code (per piece) n49 3700 25 % 960 2290 < 0,50 (50 mt, 500 khz, 100 ?c) b66285-g-x149 (elp core) b66285-p-x149 (i core) n87 5200 25 % 1360 3430 < 1,25 (200 mt, 100 khz, 100 ?c) b66285-g-x187 (elp core) b66285-p-x187 (i core) material relationship between air gap C a l value calculation of saturation current k1 (25 ?c) k2 (25 ?c) k3 (25 ?c) k4 (25 ?c) k3 (100 ?c) k4 (100 ?c) n87 134 C 0,806 243 C 0,796 206 C 0,873 fek0339-r 5 0,1 3 3,20,1 r0,8 5,70,1 16,8 0,4 15,8 0,3 21,8 0,4 fek0340-u 15,80,3 2,50,1 21,80,4 elp 22/6/16 with i 22/2,5/16 core and accessories b66285 b65804
|